Investigation of the hot ductility of a high-strength boron steel
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, cilt.608, ss.90-94, 2014 (SCI-Expanded, Scopus)
- Yayın Türü: Makale / Tam Makale
- Cilt numarası: 608
- Basım Tarihi: 2014
- Doi Numarası: 10.1016/j.msea.2014.04.053
- Dergi Adı: MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
- Sayfa Sayıları: ss.90-94
- Anahtar Kelimeler: Hot ductility, Mechanical properties, Al-Si-coated 22MnB5, Dynamic recrystallisation, Fractography, TENSILE DEFORMATION BEHAVIORS, CONSTITUTIVE MODEL
- Bursa Uludağ Üniversitesi Adresli: Evet
Özet
In this study, the high-temperature ductility behaviour of an Al-Si-coated 22MnB5 sheet was investigated. The mechanical properties of Al-Si-coated 22MnB5 boron steel were examined via hot tensile tests performed at temperatures ranging from 400 to 900 degrees C at a strain rate of 0.083 s(-1). The deformation and fracture mechanisms under hot tensile testing were considered in relation to the testing data and to the fracture-surface observations performed via SEM. The hot ductility of the tested boron steel was observed as a function of increasing temperature and the Al-Si-coated 22MnB5 boron steel exhibited a ductility loss at 700 degrees C. (C) 2014 Elsevier B.V. All rights reserved.