Phase separation and glass forming ability of (Fe0.72Mo0.04B0.24)(100-x)Gd-x (x=4, 8) bulk metallic glasses


Sarlar K., KÜÇÜK İ.

JOURNAL OF NON-CRYSTALLINE SOLIDS, cilt.447, ss.198-201, 2016 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 447
  • Basım Tarihi: 2016
  • Doi Numarası: 10.1016/j.jnoncrysol.2016.06.003
  • Dergi Adı: JOURNAL OF NON-CRYSTALLINE SOLIDS
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.198-201
  • Bursa Uludağ Üniversitesi Adresli: Evet

Özet

The effect of Gd addition on the Glass Forming Ability (GFA), magnetic and thermal properties in (Fe0.72Mo0.04B0.24)(100-x)Gd-x (x = 4, 8) bulk metallic glasses were investigated. The examined amorphous alloys'. structural, thermal and magnetic properties were investigated by using X-ray diffraction (XRD), scanning electron mi-croscopy (SEM) differential scanning calorimeter (DSC) and vibrating sample magnetometer (VSM). The results show that molten (Fe0.72Mo0.04B0.24)(92)Gd-8 presents the fully amorphous structure and solidifies into two different Fe-rich and B-rich amorphous phases. The DSC curve shows that the (Fe0.72Mo0.04B0.24)(92)Gd-8 has supercooled liquid region (Delta T-x) of about 70 K and the saturation magnetization (J(s)) and coercivity (H-c) for as-cast bulk metallic glasses (BMGs) was 0.53 T and 223 A/m respectively. (C) 2016 Elsevier B.V. All rights reserved.